PP+EPDM-T25 Impact Modified Polypropylene (Warm Black)

Higher filler loading with impact modification, giving improved stiffness and heat resistance for exterior parts with tighter dimensional demands.

PP+EPDM-T25PP Modified PolypropyleneQingdao plant

PP+EPDM-T25 Impact Modified Polypropylene (Warm Black)

Grade: PP+EPDM-T25

Family: PP Modified Polypropylene

Form: Pellets, 25 kg bags

MOQ: 500 kg

Typical Properties (TDS)

Values are typical and measured under standard ISO methods; refer to the lot COA for release data.
Property	Unit	Typical value
Density	g/cm³	1.09
MFR (230°C/2.16kg)	g/10min	10
Tensile strength	MPa	22
Flexural modulus	MPa	2100
Notched impact (23°C)	kJ/m²	30
HDT (0.45 MPa)	°C	110
Mould shrinkage	%	0.8-1.1

Typical value ranges are for grade screening and preliminary comparison. Purchases are governed by the agreed technical specification or sealed reference sample, with a COA shipped on every lot.

Recommended Processing

Parameter	Recommended
Barrel temp.	205-235°C
Mould temp.	30-50°C

Typical Applications

Automotive exterior
Wheel arch liners
Appliance structural parts

Other Grades in This Family

PP+EPDM-T20

PP+EPDM-T20 Impact Modified Polypropylene (YS269 Light Grey)

EPDM toughened with talc filling; notched impact 8 kJ/m² at -30 °C (35 kJ/m² at 23 °C), used for bumpers, exterior trim and outdoor products.

Request Data Sheet & Quote →

PP-TD20

Automotive Grade PP-TD20 (CP323)

20% talc filled polypropylene with improved stiffness and heat resistance and stable shrinkage, for automotive interior and structural parts.

Request Data Sheet & Quote →

PP CP323

Modified PP Black CP323

General purpose black modified polypropylene balancing stiffness and flow, suitable for a wide range of injection moulded structural parts.

Request Data Sheet & Quote →

PP GP-1435

Modified Polypropylene Cold Grey GP-1435

Modified polypropylene for both extrusion and injection, with low-temperature resistance, high strength and dimensional stability.

Request Data Sheet & Quote →

Need the full data sheet and a quote for PP+EPDM-T25?

Tell us the wall thickness, service temperature and volume, and we will come back within 24 hours with a technical recommendation and pricing.

Free Sample Chat on WhatsApp

FAQ

What are the typical properties of PP+EPDM-T25 Impact Modified Polypropylene (Warm Black)?

Typical properties of PP+EPDM-T25 Impact Modified Polypropylene (Warm Black) (ISO test methods; indicative values — refer to the batch COA for certified results):Density 1.09 g/cm³；MFR (230°C/2.16kg) 10 g/10min；Tensile strength 22 MPa；Flexural modulus 2100 MPa；Notched impact (23°C) 30 kJ/m²；HDT (0.45 MPa) 110 °C；Mould shrinkage 0.8-1.1 %；Parameter Recommended；Barrel temp. 205-235°C

What injection moulding conditions are recommended for PP+EPDM-T25 Impact Modified Polypropylene (Warm Black)?

Recommended processing conditions for PP+EPDM-T25 Impact Modified Polypropylene (Warm Black):Mould temp. 30-50°C

What is PP+EPDM-T25 Impact Modified Polypropylene (Warm Black) typically used for?

PP+EPDM-T25 Impact Modified Polypropylene (Warm Black) is typically used in:Automotive exterior、Wheel arch liners、Appliance structural parts

What is the minimum order quantity for PP+EPDM-T25 Impact Modified Polypropylene (Warm Black)?

Minimum order quantity is 500 kg for standard grades and 1 tonne for newly developed custom formulations.

Can PP+EPDM-T25 Impact Modified Polypropylene (Warm Black) be tailored to specific performance targets?

Yes. Qingdao Yunsu adjusts formulations to the target requirements, including glass fibre loading, flame-retardant class, UV and weathering resistance, antistatic or conductive properties and colour, and supports dedicated grade development.

How long do sampling and mass production take?

Sampling takes 3-7 days for existing grades and 7-15 days for new formulations; mass production runs 10-20 days after sample approval, shipping from Qingdao Port.