ABS WA-2031
Weather Resistant ABS WA-2031
UV stabilised system with long-term stability for outdoor products and long-life housing components.
Request Data Sheet & Quote →PC/ABS GP-1238
PC/ABS GP-1238. Tensile strength 53 MPa, Notched impact 650 J/m. MOQ 500 kg.
Typical Properties (TDS)
| Property | Unit | Typical value |
|---|---|---|
| Density (23℃) | g/cm³ | 1.155 |
| Mould shrinkage (23℃) | % | 0.3-0.5 |
| MFR (260℃/2.16kg) | g/10min | 6 |
| Tensile strength (50mm/min) | MPa | 53 |
| Elongation at break (50mm/min) | % | 35 |
| Flexural strength (2.0mm/min) | MPa | 75 |
| Flexural modulus (2.0mm/min) | MPa | 2250 |
| Notched impact strength (23℃) | J/m | 650 |
| HDT (0.45MPa) | °C | 110 |
| Flammability (–) | — | HB |
Typical value ranges are for grade screening and preliminary comparison. Purchases are governed by the agreed technical specification or sealed reference sample, with a COA shipped on every lot.
Recommended Processing
| Parameter | Recommended |
|---|---|
| Drying | 80℃, 4.0h |
| Rear zone temperature | 220℃-240℃ |
| Middle zone temperature | 230℃-250℃ |
| Front zone temperature | 240℃-260℃ |
| Nozzle temperature | 240℃-260℃ |
| Melt temperature | 230℃-250℃ |
| Mould temperature | 60℃-80℃ |
Typical Applications
- Precision electronics housings
- Explosion-protected parts
- Instrument cases
Other Grades in This Family
ABS White
Modified ABS White
General purpose white ABS with good processing behaviour and high surface gloss for appliance housings and consumer products.
Request Data Sheet & Quote →Need the full data sheet and a quote for GP-1238?
Tell us the wall thickness, service temperature and volume, and we will come back within 24 hours with a technical recommendation and pricing.
FAQ
Can PC/ABS GP-1238 replace the grade we are using now?
Yes. Send us the incumbent grade and the critical values (tensile strength, impact at −30 °C, shrinkage, colour) and we match the formulation to those targets. Most customers validate with a 5–25 kg sample before switching production.
Why can two compounds with the same grade name differ by 15% in strength?
Fibre length retention and the coupling system. We control shear on twin-screw lines and test every lot for MFR, ash, tensile and impact; each lot ships with a COA for traceability.
What are the typical properties of PC/ABS GP-1238?
Typical properties of PC/ABS GP-1238 (ISO test methods; indicative values — certified results in the batch COA):Density 1.155 g/cm³; Mould shrinkage 0.3-0.5 %; MFR 6 g/10min; Tensile strength 53 MPa; Elongation at break 35 %; Flexural strength 75 MPa; Flexural modulus 2250 MPa; Notched impact strength 650 J/m; HDT 110 °C; Flammability HB
What injection moulding conditions are recommended for PC/ABS GP-1238?
Recommended processing conditions for PC/ABS GP-1238:Drying 80℃, 4.0h; Rear zone temperature 220℃-240℃; Middle zone temperature 230℃-250℃; Front zone temperature 240℃-260℃; Nozzle temperature 240℃-260℃; Melt temperature 230℃-250℃; Mould temperature 60℃-80℃
What is PC/ABS GP-1238 typically used for?
PC/ABS GP-1238 is typically used in:Precision electronics housings, Explosion-protected parts, Instrument cases
What is the minimum order quantity for PC/ABS GP-1238?
Minimum order quantity is 500 kg for standard grades and 1 tonne for newly developed custom formulations.
Can PC/ABS GP-1238 be tailored to specific performance targets?
Yes. Qingdao Yunsu adjusts formulations to the target requirements, including glass fibre loading, flame-retardant class, UV and weathering resistance, antistatic or conductive properties and colour, and supports dedicated grade development.
How long do sampling and mass production take?
Sampling takes 3-7 days for existing grades and 7-15 days for new formulations; mass production runs 10-20 days after sample approval, shipping from Qingdao Port.
Can the color and properties be customized to our requirements?
Yes. Colours can be matched to your colour standard. Give us the working conditions, performance targets and cost ceiling — we design the formulation backwards from there. Most customers validate with a 5–25 kg sample before series production.