30% glass fibre reinforced: tensile strength 165 MPa, flexural modulus 8500 MPa, notched impact 11 kJ/m², for load-bearing parts and power tool housings.
| Property | Unit | Typical value |
|---|---|---|
| Density | g/cm³ | 1.36 |
| Tensile strength | MPa | 165 |
| Elongation at break | % | 3.0 |
| Flexural strength | MPa | 240 |
| Flexural modulus | MPa | 8500 |
| Notched impact (23°C) | kJ/m² | 11 |
| HDT (1.82 MPa) | °C | 205 |
| Flammability | UL94 | HB |
| Mould shrinkage | % | 0.3-0.6 |
| Parameter | Recommended |
|---|---|
| Drying | 80-90°C × 4-6 h |
| Barrel temp. | 250-275°C |
| Mould temp. | 70-90°C |
| Injection pressure | 70-110 MPa |
Glass fibre reinforced and impact modified: tensile strength 155 MPa, notched impact 8 kJ/m² at -30 °C, for power tools, garden equipment and industrial housings.
Request Data Sheet & Quote →
Glass fibre reinforcement combined with elastomer toughening: tensile strength 140 MPa, notched impact 18 kJ/m², for drop-tested and shock-loaded parts.
Request Data Sheet & Quote →Tell us the wall thickness, service temperature and volume, and we will come back within 24 hours with a technical recommendation and pricing.