PA6-GF30
Reinforced Nylon PA6 GF30 (Gold)
30% glass fibre reinforced: tensile strength 165 MPa, flexural modulus 8500 MPa, notched impact 11 kJ/m², for load-bearing parts and power tool housings.
Request Data Sheet & Quote →Reinforced & Toughened Nylon PA6
Glass fibre reinforcement combined with elastomer toughening: tensile strength 140 MPa, notched impact 18 kJ/m², for drop-tested and shock-loaded parts.
Typical Properties (TDS)
| Property | Unit | Typical value |
|---|---|---|
| Density | g/cm³ | 1.30 |
| Tensile strength | MPa | 140 |
| Elongation at break | % | 5.0 |
| Flexural strength | MPa | 200 |
| Flexural modulus | MPa | 6500 |
| Notched impact (23°C) | kJ/m² | 18 |
| HDT (1.82 MPa) | °C | 190 |
| Flammability | UL94 | HB |
Typical value ranges are for grade screening and preliminary comparison. Purchases are governed by the agreed technical specification or sealed reference sample, with a COA shipped on every lot.
Recommended Processing
| Parameter | Recommended |
|---|---|
| Drying | 80-90°C × 4-6 h |
| Barrel temp. | 245-270°C |
| Mould temp. | 60-85°C |
Typical Applications
- Tool housings
- Industrial fittings
- Sports equipment
- Non-structural automotive
Other Grades in This Family
PA6-GF30 HI
High-Impact Reinforced Nylon PA6 GF30 (Green)
Glass fibre reinforced and impact modified: tensile strength 155 MPa, notched impact 8 kJ/m² at -30 °C, for power tools, garden equipment and industrial housings.
Request Data Sheet & Quote →Need the full data sheet and a quote for PA6-GF25 HI?
Tell us the wall thickness, service temperature and volume, and we will come back within 24 hours with a technical recommendation and pricing.
FAQ
What are the typical properties of Reinforced & Toughened Nylon PA6?
Typical properties of Reinforced & Toughened Nylon PA6 (ISO test methods; indicative values — refer to the batch COA for certified results):Density 1.30 g/cm³；Tensile strength 140 MPa；Elongation at break 5.0 %；Flexural strength 200 MPa；Flexural modulus 6500 MPa；Notched impact (23°C) 18 kJ/m²；HDT (1.82 MPa) 190 °C；Flammability HB UL94；Parameter Recommended
What injection moulding conditions are recommended for Reinforced & Toughened Nylon PA6?
Recommended processing conditions for Reinforced & Toughened Nylon PA6:Drying 80-90°C × 4-6 h；Barrel temp. 245-270°C；Mould temp. 60-85°C
What is Reinforced & Toughened Nylon PA6 typically used for?
Reinforced & Toughened Nylon PA6 is typically used in:Tool housings、Industrial fittings、Sports equipment、Non-structural automotive
What is the minimum order quantity for Reinforced & Toughened Nylon PA6?
Minimum order quantity is 500 kg for standard grades and 1 tonne for newly developed custom formulations.
Can Reinforced & Toughened Nylon PA6 be tailored to specific performance targets?
Yes. Qingdao Yunsu adjusts formulations to the target requirements, including glass fibre loading, flame-retardant class, UV and weathering resistance, antistatic or conductive properties and colour, and supports dedicated grade development.
How long do sampling and mass production take?
Sampling takes 3-7 days for existing grades and 7-15 days for new formulations; mass production runs 10-20 days after sample approval, shipping from Qingdao Port.