PA6-GF30
Reinforced Nylon PA6 GF30 (Gold)
30% glass fibre reinforced: tensile strength 165 MPa, flexural modulus 8500 MPa, notched impact 11 kJ/m², for load-bearing parts and power tool housings.
Request Data Sheet & Quote →High-Impact Reinforced Nylon PA6 GF30 (Green)
Glass fibre reinforced and impact modified: tensile strength 155 MPa, notched impact 8 kJ/m² at -30 °C, for power tools, garden equipment and industrial housings.
Typical Properties (TDS)
| Property | Unit | Typical value |
|---|---|---|
| Density | g/cm³ | 1.37 |
| Tensile strength | MPa | 155 |
| Elongation at break | % | 4.5 |
| Flexural strength | MPa | 225 |
| Flexural modulus | MPa | 7800 |
| Notched impact (23°C) | kJ/m² | 16 |
| Notched impact (-30°C) | kJ/m² | 8 |
| HDT (1.82 MPa) | °C | 200 |
| Flammability | UL94 | HB |
Typical value ranges are for grade screening and preliminary comparison. Purchases are governed by the agreed technical specification or sealed reference sample, with a COA shipped on every lot.
Recommended Processing
| Parameter | Recommended |
|---|---|
| Drying | 80-90°C × 4-6 h |
| Barrel temp. | 250-275°C |
| Mould temp. | 70-90°C |
| Injection speed | Medium-high |
Typical Applications
- Power tool housings
- Garden equipment
- Low-temperature parts
- Industrial housings
Other Grades in This Family
PA6-GF25 HI
Reinforced & Toughened Nylon PA6
Glass fibre reinforcement combined with elastomer toughening: tensile strength 140 MPa, notched impact 18 kJ/m², for drop-tested and shock-loaded parts.
Request Data Sheet & Quote →Need the full data sheet and a quote for PA6-GF30 HI?
Tell us the wall thickness, service temperature and volume, and we will come back within 24 hours with a technical recommendation and pricing.
FAQ
What are the typical properties of High-Impact Reinforced Nylon PA6 GF30 (Green)?
Typical properties of High-Impact Reinforced Nylon PA6 GF30 (Green) (ISO test methods; indicative values — refer to the batch COA for certified results):Density 1.37 g/cm³；Tensile strength 155 MPa；Elongation at break 4.5 %；Flexural strength 225 MPa；Flexural modulus 7800 MPa；Notched impact (23°C) 16 kJ/m²；Notched impact (-30°C) 8 kJ/m²；HDT (1.82 MPa) 200 °C；Flammability HB UL94
What injection moulding conditions are recommended for High-Impact Reinforced Nylon PA6 GF30 (Green)?
Recommended processing conditions for High-Impact Reinforced Nylon PA6 GF30 (Green):Parameter Recommended；Drying 80-90°C × 4-6 h；Barrel temp. 250-275°C；Mould temp. 70-90°C；Injection speed Medium-high
What is High-Impact Reinforced Nylon PA6 GF30 (Green) typically used for?
High-Impact Reinforced Nylon PA6 GF30 (Green) is typically used in:Power tool housings、Garden equipment、Low-temperature parts、Industrial housings
What is the minimum order quantity for High-Impact Reinforced Nylon PA6 GF30 (Green)?
Minimum order quantity is 500 kg for standard grades and 1 tonne for newly developed custom formulations.
Can High-Impact Reinforced Nylon PA6 GF30 (Green) be tailored to specific performance targets?
Yes. Qingdao Yunsu adjusts formulations to the target requirements, including glass fibre loading, flame-retardant class, UV and weathering resistance, antistatic or conductive properties and colour, and supports dedicated grade development.
How long do sampling and mass production take?
Sampling takes 3-7 days for existing grades and 7-15 days for new formulations; mass production runs 10-20 days after sample approval, shipping from Qingdao Port.